Sorption and solubility of bioceramic endodontic sealers and sealer based on epoxy resin
DOI:
https://doi.org/10.33448/rsd-v10i7.16676Keywords:
Endodontics; Solubility; Root canal filling.Abstract
Introduction: Endodontic cements are used in root canal filling and are associated with successful endodontic treatment, filling the spaces between the walls of the root canal and gutta-percha. The sorption and solubility of these materials are properties that are related to the process of remineralization of periapical tissues and antimicrobial capacity, in addition to being parameters linked to deleterious effects, such as cement degradation and the consequent recontamination of the root canal. Methods: AH Plus cements (Dentsply, São Paulo, SP, Brazil), MTA Fillapex (Angelus, Londrina, PR, Brazil) and Bio-C Sealer (Angelus, Londrina, PR, Brazil) were handled following the manufacturer's instructions and stored in an oven at 37°. Subsequently, they were weighed on a precision analytical balance so that the samples were then placed in distilled water for 24 hours in an oven at 37° and thus, after removing the excess, the samples underwent sorption and solubility tests, and the averages were compared by Tukey HSD test. Results: regarding sorption, it was observed that MTA Fillapex had the highest value, whereas the other cements had lower values and no statistically significant differences between them. AH-Plus cement had the lowest solubility value, while Bio–C cement had the highest. Conclusions: Even with values higher than those recommended by ISO standards, Bio-C and MTA-Fillapex cements are still suitable for clinical use.
References
Alonso, F. S., Gomes, C. C., Freitas, L. F., Gomes, I. C., Pinto, S. S. & Penina, P. (2005). Análise comparativa do escoamento de dois cimentos endodônticos: Endofil e AH-Plus. UFES revista de odontologia, 7(1), 48-54, 2005. Retrieved from https://docs.bvsalud.org/biblioref/2019/02/689141/analise.pdf
Coomaraswamy, K. Lumley, P. & Hofmann, M. (2007) Effect of Bismuth Oxide Radioopacifier Content on the Material Properties of an Endodontic Portland Cement–based (MTA-like) System. Journal of Endodontics, 33(3), 295–298. doi:10.1016/j.joen.2006.11.018
De Deus, G., Gurgel Filho, E. D., Ferreira, C. M. & Coutinho Filho, T. (2002). Penetração intratubular de cimentos endodônticos. Pesquisa Odontológica Brasileira, 16(4), 332-336. doi: 10.1590/S1517-74912002000400009
Dourado TTH (2017). Análise da literatura científica especializada das propriedades físicas, químicas e biológicas dos cimentos biocerâmicos. [Trabalho de conclusão de curso, Universidade Federal da Paraíba]. Retrieved from https://repositorio.ufpb.br/jspui/handle/123456789/12478
Grech, L., Mallia, B. & Camilleri, J. (2013). Investigation of the physical properties of tricalcium silicate cement-based root-end filling materials. Dent Mater, 29(2), 20-28. doi:10.1016/j.dental.2012.11.007
International Organization for Standardization. (2012). Dental Root Canal Sealing Materials (ISO Standard No. 6876:2012).
Kopper, P. M. P. (2008). Estudo da capacidade de selamento do AH-Plus, Endorez e Real Seal, em canais radiculares de cães expostos ao meio bucal por meio da avaliação da resposta inflamatória periapical. [Doutorado em Clínica Odontológica – Área de Concentração Endodontia, Universidade Federal do Rio Grande do Sul]. Retrieved from https://www.lume.ufrgs.br/bitstream/handle/10183/49730/000658895.pdf?sequence=1
Lima, N. F. F., Santos, P. R. N., Pedrosa, M. S. & Delboni, M. G. (2017) Cimentos biocerâmicos em endodontia: revisão de literatura. Revista da Faculdade de Odontologia UPF, 22(2), 248-254. doi: https://doi.org/10.5335/rfo.v22i2.7398
Martins, C. R., Lopes, W. A. & Andrade, J. B. (2013). SOLUBILIDADE DAS SUBSTÂNCIAS ORGÂNICAS. Química Nova, 36(8), 1248-1255. doi: 10.1590/S0100-40422013000800026
Mendes, A. T., Silva, P. B., Só, B. B., Hashizume, L. N., Vivan, R. R., Rosa, R. A., Duarte, M. A. H. & Só, M. V. R. (2018). Evaluation of Physicochemical Properties of New Calcium Silicate - Based Sealer. Brazilian Dental Journal, 29(6), 536-540. doi: 10.1590/0103-6440201802088
Nascimento Sobrinho, G. A. (2014). Estudo da sorção e da contribuição da troca iônica na dinâmica do Cs em solos altamente intemperizados. [Dissertação, Instituto de Radioterapia de Dosimetria do Rio de Janeiro]. Retrieved from http://moodle.ird.gov.br/ensino/images/DissertacoesMestrado/Dissert.Mestrado2014/dissertao_guilherme%20augusto%20nascimento%20sombrinho.pdf
Oliveira, P. H. C. (2017). Biocompatibilidade e capacidade de mineralização de um cimento Biocerâmico experimental. Estudo em tecido subcutâneo de ratos. [Trabalho de conclusão de curso, Faculdade de Odontologia de Araçatuba]. Retrieved from https://repositorio.unesp.br/handle/11449/156747
Razdan, A., Benetti, A. R. & BJØRNDAL, L. (2019) Do in vitro solubility studies on endodontic sealers demonstrate a high level of evidence? A systematic review. Acta Odontologica Scandinavica, Scandinavia, 77(4), 253-263. doi: 10.1080/00016357.2018.1538535
Santos, A. F. (2019). Avaliação da viabilidade celular de fibroblastos L929 e da resposta inflamatória em tecido subcutâneo de ratos ao novo material Bio-C Pulpo. [Dissertação, Universidade Federal de Alfenas]. Retrieved from https://bdtd.unifal-mg.edu.br:8443/handle/tede/1362
Sousa, N. B., Nunes, M. A. C., Veloso, K. M. M. & Pereira, A. F. V. (2014). Agregado de trióxido mineral e uso como material retro-obturador em cirurgia paraendodôntica. Revista Brasileira de Odontologia, 71(2), 144-147. Retrieved from http://revodonto.bvsalud.org/scielo.php?script=sci_arttext&pid=S0034-72722014000200006
Torres, F. F. E. (2016). Testes convencionais e empregando micro-ct na avaliação de propriedades físico-químicas de materiais retrobturadores e cimentos endodônticos. [Dissertação, Faculdade de Odontologia de Araraquara]. Retrieved from https://repositorio.unesp.br/handle/11449/138247
Viapiana, R., Flumignan, D. L., Guerreiro-Tanomaru, J. M., Camilleri, J. & Tanomaru-Filho, M. (2013). Physicochemical and mechanical properties of zirconium oxide and niobium oxide modified Portland cement-based experimental endodontic sealers. International Endodontic Journal, 47(5), 437-448. doi: 10.1111/iej.12167
Vitti, R. P., Prati, C., Sinhoreti, M. A. C., Zanchi, C. H., Silva, M. G. S., Ogliari, F. A. & Gandolfi, M. G. (2013). Chemical-physical properties of experimental root canal sealers based on butyl ethylene glycol disalicylate and MTA. Dental Materials, 29(12), 1287-1294. doi: 10.1016/j.dental.2013.10.002
Zhou, H. M., Shen, Y., Zheng, W., Li, L., Zheng, Y. F. & Haapasalo, M. (2013). Physical Properties of 5 Root Canal Sealers. Journal of Endodontics, 39(10), 1281-1286. doi: 10.1016/j.joen.2013.06.012
Zordan-Bronzel, C. L., Torres, F. F. E., Tanomaru-Filho, M., Chávez-Andrade, G. M., Bosso-Martelo, R. & Guerreiro-Tanomaru, J. M. (2019). Evaluation of Physicochemical Properties of a New Calcium Silicate–based Sealer, Bio-C Sealer. Journal of Endodontics, 45(10), 1248-1252. doi: 10.1016/j.joen.2019.07.006
Zvi, M., Bettina, B. & Harold, E. G. (2011) Instrumentos, Materiais e Aparelhos. In: K. M. Hargreaves & S. Cohen (10ª ed.), Caminhos da Polpa (pp. 250-264). Rio de Janeiro, Brasil: Elsevier.)
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2021 Lucas Adriano Pascuti Bastos ; Rafael Pino Vitti; Homero Casonato Junior
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors who publish with this journal agree to the following terms:
1) Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
2) Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
3) Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.