Analysis of the biomimetic properties of niobium silicate incorporated into dental materials – literature review
DOI:
https://doi.org/10.33448/rsd-v12i5.41777Keywords:
Niobium; Biomimetics; Dental materials; Dentistry.Abstract
Introduction: The development of strategies for biomimetic remineralization is presented as an extremely advantageous alternative to current restorative procedures. Niobium is a metal that, even when applied in small amounts, shows potential to improve the properties of different materials, in addition to presenting high biocompatibility and improving the physical and optical properties of these materials, in addition to presenting low toxicity. Objective: To evaluate the biomimetic properties of niobium silicate, when incorporated into dental materials, such as composite resins, cements and adhesives. Methodology: An integrative literature review was carried out in the PubMed, SCIELO and Google Scholar databases with the descriptors: Niobium Silicate, Biomimetics, Dental Materials and Dentistry. Results: Information was found in the literature indicating that Niobium Silicate is a viable alternative in the study of bioactive agents added to dental materials. Conclusion: Given the above, it can be concluded that niobium silicate presents satisfactory results and biocompatible characteristics when incorporated into composite resin, resin cement, adhesives and dental substrate.
References
Almeida, G. C., Barros, J. C., & Monteiro, R. D. S. (2019). Nióbio: o elemento do século XXI. São Paulo: Sociedade Brasileira de Química, 59.
Alves, A. R., & Coutinho, A. D. R. (2015). The evolution of the niobium production in Brazil. Materials Research, 18, 106-112.
Arinelli, A. M. D., Pereira, K. F., Prado, N. A. S., & Rabello, T. B. (2016). Sistemas adesivos atuais. Revista Brasileira de Odontologia, 73(3), 242.
Balbinot, G. S., Leitune, V. C. B., Ogliari, F. A., & Collares, F. M. (2020). Niobium silicate particles promote in vitro mineral deposition on dental adhesive resins. Journal of Dentistry, 101, 103449.
Bosso, R. (2014). Avaliação de propriedades físicas, químicas e biológicas de cimentos Portland associados a radiopacificadores micro e nanoparticulados (doctoral dissertation).
Bruziquesi, C. G., Balena, J. G., Pereira, M. C., Silva, A. C., & Oliveira, L. C. (2020). Nióbio: um elemento químico estratégico para o Brasil. Química nova, 42, 1184-1188.
Carneiro, K. K., Meier, M. M., Santos, C. C. D., Maciel, A. P., Carvalho, C. N., & Bauer, J. (2016). Adhesives doped with bioactive niobophosphate micro-filler: degree of conversion and microtensile bond strength. Brazilian dental journal, 27, 705-711.
Carvalho, J. G. D., Godoy, L. F. D., & Bastos, M. T. A. A. (2002). Comparação de duas técnicas para remineralização do esmalte. Pesquisa Odontológica Brasileira, 16, 89-92.
Farias, Í. D. L. (2023). Síntese e caracterização de um cimento a base de hidroxiapatita dopado com óxido de nióbio para uso em procedimentos de regeneração óssea.
Figueiredo, E. Z. D. (2019). Avaliação do silicato de nióbio como partícula de carga em cimento resinoso fotopolimerizável experimental.
Griffith, W. P., & Morris, P. J. (2003). Charles Hatchett FRS (1765-1847), chemist and discoverer of niobium. Notes and Records of the Royal Society of London, 57(3), 299-316.
Leitune, V. C. B., Collares, F. M., Takimi, A., de Lima, G. B., Petzhold, C. L., Bergmann, C. P., & Samuel, S. M. W. (2013). Niobium pentoxide as a novel filler for dental adhesive resin. Journal of dentistry, 41(2), 106-113.
Machado, A. L. S. (2018). Influência da incorporação de silicato de nióbio como carga inorgânica para uma resina composta.
Mestieri, L. B. (2014). Estudo das células primárias dentais, viabilidade celular e bioatividade de materiais á base de silicato de cálcio.
Mestieri, L. B., Gomes-Cornélio, A. L., Rodrigues, E. M., Faria, G., Guerreiro-Tanomaru, J. M., & Tanomaru-Filho, M. (2017). Cytotoxicity and bioactivity of calcium silicate cements combined with niobium oxide in different cell lines. Brazilian Dental Journal, 28, 65-71.
Nogueira, F. S. (2017). A influência das técnicas de remineralização biomimética da dentina na durabilidade da união dentina-resina.
Pereira, T. A. V. (2018). Nanopartículas de óxidos de ferro e nióbio com diferentes recobrimentos: síntese, caracterização e avaliação do potencial biológico (Doctoral dissertation, Universidade de São Paulo).
Pinto, L. D. (2021). Influência da adição de silicato de nióbio nas características fisico-químicas de um adesivo ortodôntico experimental.
Ramos, N. M. (2021). Remineralização Biomimética: o futuro da Medicina Dentária Conservadora (Doctoral dissertation, Universidade do Porto (Portugal)).
Roveda, F. P. (2018). Influência do silicato de nióbio como partícula de carga na cimentação de lâminas cerâmicas sobre esmalte dentário.
Silva, R. A. (2022). Avaliação das propriedades físico-químicas e osteogênicas do cimento portland associado ao pentóxido de nióbio (Master's thesis, Universidade Federal do Rio Grande do Norte).
Sousa, L. N., Moura, M. E. M., Mendonça, J. S., Nobre, N. E. C., Quirino, A. B. G., Silva, F. B., & Nojosa, J. S. (2017). Remineralização Dentinária Através do Uso de Análogo Biomiméticos. Journal of Health Sciences, 19(5), 283-283.
Wisniak, J. (2015). Charles Hatchett: The discoverer of niobium. Educación química, 26(4), 346-355.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2023 Jullyana Oliveira Galvão de Sousa ; Leandra da Silva Negreiros; Luanne Mara Rodrigues de Matos; Marconi Raphael de Siqueira Rego; Matheus Araújo Brito Santos Araujo
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors who publish with this journal agree to the following terms:
1) Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
2) Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
3) Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.