Influence of welding current variation on the geometric characteristics of the weld bead in CA50 rebar steel using shielded metal arc welding and MIG/MAG Processes with overlay joint
DOI:
https://doi.org/10.33448/rsd-v13i8.46489Keywords:
Heat input; CA50 rebar welding; Overlay welding; Shielded metal arc welding and MIG/MAG welding.Abstract
The construction industry is an important parameter of economic development, driving the search for techniques and products with improved performance. Weldable rebar steels are widely used in the construction sector, especially in reinforced concrete, due to their diverse mechanical properties. CA50 steel is widely known for its weldability, which instills confidence in the structure. Therefore, this study aims to investigate the heat input and geometric characteristics of welded joints using shielded metal arc welding and MIG/MAG processes with overlay joint, employing three different welding current variations. Approximately 100mm samples of CA50 rebar steel were prepared and welded using AWS E11018-M covered electrode and MIG/MAG. The weld bead had a length of 100mm with equal spacing according to ABNT NBR 6118:2003 standard. Welding time was measured to calculate heat input, and the samples were cut horizontally using a band saw. Metallographic procedures for revealing the macrography of the fusion zone (FZ) and heat-affected zone (HAZ) utilized optical microscopy techniques. It is concluded that overlay welding of CA50 rebar steel with shielded metal arc welding did not exhibit good geometric aspects such as penetration and weld width at low welding currents, while the MIG/MAG process indicated good welding characteristics at the current parameters, thus enabling rebar welding with overlay joint in the construction sector using the parameters employed.
References
Alonso, M. B (2006). Caracterização de união por solda de tôpo em barras CA-50 com eletrodos revestidos (Doctoral dissertation, Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia Mecânica.).
Andrade, A. D. S., Medeiros, J. L. B., Biehl, L. V., Souza, J. D., Pacheco, D. D. J., & Martins, C. O. D. (2023). Análise mecânica e metalúrgica da união soldada entre um aço inoxidável duplex S32205 com metal de adição de aço inoxidável superaustenítico ER-385-904L. Matéria (Rio de Janeiro), 28, e20220307.
Araújo, F. D. A., Amorim, M. O. D., Cruz, R. M. D. A., Alves, A. D. N. S., Brandi, S. D., & Soeiro, J. C. (2023). Análise da soldagem multipasse utilizando delineamento experimental na manutenção de aço ASTM A131 Grau A. Matéria (Rio de Janeiro), 27(2), e13210.
Associação Brasileira De Normas Técnicas. NBR 6118 (2003). Projeto de estruturas de concreto - Procedimento.
Aws (2012). Specification for Carbon Steel Electrodes for Shielded Metal Arc Welding, American Welding Society, Doral.
Barbosa, L. H. S., Modenesi, P. J., Godefroid, L. B., & Borba, T. M. D. (2018). Microestrutura e características mecânicas da zona fundida de um aço naval soldado ao arco submerso com aporte térmico muito elevado. Soldagem & Inspeção, 23, 168-179.
Bottesini, A. (2010). Ensaio de Dobramento, UPF.
Daroit, R. S. (2012). Análise de estruturas viscoelásticas [dissertação de mestrado]. Porto Alegre: Universidade Federal do Rio Grande do Sul.
Silverio, M. G., Raposo, L. H. A., Lopes, R. T., & Júnior, P. C. S. (2021). Evaluation of X-shaped welded joints with Co-Cr alloy under different welding parameters: Analysis by micro-CT and flexural strength. Research, Society and Development, 10(4), e44510414308-e44510414308.
DebRoy, T., & David, S. A. (1995). Physical processes in fusion welding. Reviews of modern physics, 67(1), 85.
Farias, T. A., Silva, A. C. S. D., Figueredo, E. W. A., Pereira, M., & Silva, F. J. D. (2021). Efeito da Velocidade de Soldagem nas Características Geométricas e Microestruturais de Soldas por Arco Submerso em Tandem Arc. Soldagem & Inspeção, 26, e2609.
Fonseca, C. S., Pinheiro, I. P., & Silva, S. N. D. (2016). Influência do aporte térmico sobre a morfologia da austenita e na quantidade das fases em chapas soldadas de aço inoxidável duplex SAF2205. Matéria (Rio de Janeiro), 21(1), 227-234.
Freitas, R.; Carvalho, R.; Guedes. (2018). Análise metalográfica de um perfil soldado por eletrodo revestido. Revista Científica Semana Acadêmica. Nº. 140.
Giarollo, D. F., Hackenhaar, W., Mazzaferro, C. C., & Mazzaferro, J. A. (2022). Bead Geometry Prediction in Pulsed GMAW Welding: A Comparative Study on the Performance of Artificial Neural Network and Regression Models. Soldagem & Inspeção, 27, e2722.
Kulmann Filho, M. A. D. R., & Machado, I. G. (2024). Resistência ao Impacto Estrutural de Perfis I Soldados. Soldagem & Inspeção, 29, e2903.
Marques, P. Modenesi, P. J.; & Bracarense, A. Q. (2016). Soldagem fundamentos e tecnologia. (4a ed.), Editora UFMG.
Modenesi, P. J., Marques, P. V., & Santos, D. B. (2012). Introdução à metalurgia da soldagem. Belo Horizonte: UFMG.
Phillips, D. H. (2023). Welding engineering: an introduction. John Wiley & Sons.
Resende, A. A. D., & Scotti, A. (2015). Influência dos Níveis das Correntes, Ângulo de Inclinação da Tocha e Distância entre a Tocha ea Peça sobre a Geometria do Cordão de Solda Usando “Plasma-MIG” com Arcos Concêntricos. Soldagem & Inspeção, 20(4), 501-514.
Silva, A. C. S. D., Figueredo, E. W. A., Silva Júnior, D. C. D., Hermenegildo, T. F. D. C., & Santos, T. F. D. A. (2018). Soldagem helicoidal de tubos produzida em campo do aço ASTM A-1018 e sua correlação com características mecânicas e microestruturais das juntas soldadas. Soldagem & Inspeção, 23, 364-379.
Silva, E. B. D., & Maciel, T. M. (2023). Influência da velocidade de correntes de ar sobre a porosidade emjuntas soldadas pelo processo MIG/MAG. Matéria (Rio de Janeiro), 27, e13225.
Silva, L. G. P., de Lima, D. M., da Silva Medeiros, I., & López-Yánez, P. A. (2021). Solução estrutural de galpão em aço. Research, Society and Development, 10(8), e54810817765-e54810817765.
Silvério, M. G., Raposo, L. H. A., Lopes, R. T., & Júnior, P. C. S. (2021). Evaluation of X-shaped welded joints with Co-Cr alloy under different welding parameters: Analysis by micro-CT and flexural strength. Research, Society and Development, 10(4), e44510414308-e44510414308.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 Dnilson Silva Braga; Thiago Antônio Paixão de Sousa Costa ; Hélio Antônio Lameira de Almeida
![Creative Commons License](http://i.creativecommons.org/l/by/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors who publish with this journal agree to the following terms:
1) Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
2) Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
3) Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.