Evaluation of the rheological coating mortar behavior by the direct shear test

Authors

DOI:

https://doi.org/10.33448/rsd-v10i1.11617

Keywords:

Mortar; Fresh state; Direct shear; Resistence to simple compression; Scanning electron microscopy (SEM).

Abstract

The coating mortars behavior in its fresh state has been the object of many recent researches in Brazil. It has become, therefore, interesting the introduction of new technologies, which seek to optimize the performance of mortars, improving the knowledge of its properties, allowing a productive enforcement and minimizing, overall, future failures. The article analyzes the coating mortars’ behavior, in its fresh state, verifying the efficiency in the use of the direct shear equipment, with different combinations of traces and composing materials. Four traces of mortar were dosed, with distinct proportions of lime (TR1 = 1:0:6; TR2 = 1:0,5:6; TR3 = 1:1:6 – reference; TR4 = 1:1,5:6), presenting constant scattering (flowtable) and equal to 245 ± 5 mm. Direct shear assays were done applying different normal tensions (10 kPa, 37 kPa and 50 kPa) and shear speed of 0,2 mm/min. The method allowed to identify increase of shear tensions, cohesion, friction angle and horizontal displacements as lime is added on the mixture, indicating the sensibility of the method and great potential of use to this appraisal in mortar in its fresh state. The addition of lime in traces increases the water/cement factor for the same workability in the fresh state, but in the hardened state it can increase the porosity of mortar, causing loss of RCS. Eletromicrografhs made it possible to identify the pores, the arrangements between the constituents, the roughness of the surfaces, the interface areas between materials and the crystals present in the binder paste.

References

Allen, E., & Iano, J. (2013). Fundamentos da Engenharia de Edificações. (5a ed.). Bookman.

Almeida, R. S., Silva, F. G. S., Silva, V. S., & Gonçalves, J. P. (2013). Avaliação da resistência ao cisalhamento em argamassa à base de cimento. Cesumar, 15(1), 5-11.

American Society for Testing and Materials – ASTM (2011). ASTM 3080: Standard test method for direct shear test of soils under consolidated drained conditions. USA.

Araújo, R. C., Carasek, H., Cascudo, O., & Angelim, R. (2017). Caracterização reológica de argamassa de revestimento pelo método do cisalhamento direto. In: XII Simpósio Brasileiro de Tecnologia das Argamassas (SBTA). Anais, Brasil.

Associação Brasileira de Normas Técnicas – ABNT (2019). NBR 7215: Cimento Portland – Determinação da resistência à compressão de corpos de prova cilíndricos.

Ball, R. J., Adel, E., & Allen, G. C. (2011). Influence of carbonation on the load dependent deformation of hydraulic lime mortars. Materials Science and Engineering, 528(7-8), 3193-3199. doi:10.1016/j.msea.2010.12.070.

Campos, M. O. (2014). Estudo da resistência de aderência à tração e ao cisalhamento de revestimentos de argamassa em substratos de concreto. Dissertação de M.Sc., Brasil.

Campos, M. O., Carasek, H., Oliveira, L., Vargas, C. L., & Costa e Silva, A. J. (2015). Determinação da resistência de aderência ao cisalhamento de revestimentos de argamassa pelo método do cisalhamento direto de solos. In: XI Simpósio Brasileiro de Tecnologia das Argamassas (SBTA). Anais., Brasil.

Carasek, H. (2010). Materiais de Construção Civil e Princípios de Ciência e Engenharia de Materiais. (2a ed.): IBRACON.

Carasek, H., Araújo, R. C., Cascudo, O., & Angelim, R. (2016). Parâmetros da areia que influenciam a consistência e a densidade de massa das argamassas de revestimento. Revista Matéria, 21(3), 714-732. 10.1590/S1517-707620160003.0068

Cardoso, F. A., John, V. M. & Pileggi, R. G. (2009). Rheological behavior of mortars under different squeezing rates. Cementand Concrete Research, 39(9), 748-753. 10.1016/j.cemconres.2009.05.014

Cincotto, M. A., Marques, J. C., & Helene, P. R. L. (1985). Propriedades das argamassas de cimento: cal: areia. In: Seminário sobre argamassas. Anais., Brasil.

Gominho, M. S. L. A. (2016). Caracterização microestrutural de argamassas. Dissertação de Mestrado, Instituto Superior Técnico, Brasil.

Koche, J. C. (2011). Fundamentos de metodologia científica: teoria da ciência e iniciação à pesquisa. Petrópolis: Vozes.

Lu, G., & Wang, K. (2011). Theoretical and experimental study on shear behavior of fresh mortar. Cement and Concrete Composites, 33(2), 319-327. 10.1016/j.cemconcomp.2010.09.002

Lu, G., Wang, K., & Rudolphi, T.J. (2007). Modeling rheological behavior of highly flowtable mortar using concepts of particle and fluid mechanics. Cement and Concrete Composites, 30(1), 1-12. 10.1016/j.cemconcomp.2007.06.002

Ludke, M., & Andre, M. E. D. A. (2013). Pesquisa em educação: abordagens qualitativas: EPU.

NBR 13276(2016).: Argamassa para assentamento e revestimento de paredes e tetos – Determinação do índice de consistência. Rio de Janeiro.

NBR 13281(2005).: Argamassa para assentamento e revestimento de paredes e tetos – Requisitos. Rio de Janeiro.

NBR 16605(2017).: Cimento Portland e outros materiais em pó – Determinação da massa específica, Rio de Janeiro.

NBR 16607(2018).: Cimento Portland – Determinação dos tempos de pega. Rio de Janeiro.

NBR 6473(2003c): Cal virgem e cal hidratada – Análise química. Rio de Janeiro.

NBR 7175(2003d).: Cal hidratada para argamassas – Requisitos. Rio de Janeiro.

NBR 7211(2009b).: Agregados para concreto – Especificação. Rio de Janeiro.

NBR 9289(2000): Cal hidratada para argamassas – Determinação da finura. Rio de Janeiro.

NBR NM 248(2003b): Agregados – Determinação da composição granulométrica. Rio de Janeiro.

NBR NM 45(2006).: Agregados – determinação da massa unitária e do volume de vazios. Rio de Janeiro.

NBR NM 46(2003a): Agregados – Determinação do material fino que passa através da peneira 75 μm, por lavagem. Rio de Janeiro.

NBR NM 52(2009a).: Agregado miúdo – Determinação da massa específica e massa específica aparente. Rio de Janeiro.

Paiva, S. C., Gomes, E. A. O., & Oliveira, R. A. (2007). Controle de qualidade da cal para argamassas – metodologias alternativas. Revista Ciência & Tecnologia, 1(1), 1-11.

Pereira, A. S., Shitsuka, D. M., Parreira, F. J., & Shitsuka, R. (2018). Metodologia da pesquisa científica. (1a ed), Santa Maria: UAB/NTE.

Rubio-Hernández, F. J. (2018). Rheological behavior of fresh cement pastes. Fluids, 3(4), 106-121. 10.3390/fluids3040106

Santos, W. J. (2011). Argamassa de alto desempenho. Dissertação de Mestrado, Universidade Federal Juiz de Fora, Juiz de Fora, Brasil.

Silva, N. G. (2011). Avaliação da retração e da fissuração em revestimento de argamassa na fase plástica. Tese de Doutorado, Universidade Federal de Santa Catarina, Brasil.

Sousa, J. G. G. (2005). Contribuição ao estudo das propriedades das argamassas de revestimento no estado fresco. Tese de Doutorado, Universidade de Brasília, Brasil.

Sousa, J. G. G., & Aquino Filho, L. P. B. (2013). Caracterização de argamassas no estado fresco aplicando técnica de cisalhamento direto. Evolvere Scientia, 2(1), 68-82.

Sousa, J. G. G., & Bauer, E. (2002). Estudo da reologia das argamassas de revestimento no estado fresco. In: Congresso Brasileiro de Engenharia e Ciência dos Materiais (CBECIMAT). Anais. Rio Grande do Norte, Brasil, Nov. 2002, 571-577.

Tokarski, R. B., Matoski, A., Cechin, L., & Weber, A. M. (2018). Comportamento das argamassas de revestimento no estado fresco, compostas com areia de britagem de rocha calcária e areia natural. Revista Matéria, 23(3), e12196. 10.1590/s1517-707620180003.0530

Published

06/01/2021

How to Cite

NASCIMENTO, I. R. Q. S. .; FUCALE, S.; SILVA, A. J. da C. e; SILVA, A. C. da; FERREIRA, S. R. de M. . Evaluation of the rheological coating mortar behavior by the direct shear test. Research, Society and Development, [S. l.], v. 10, n. 1, p. e17010111617, 2021. DOI: 10.33448/rsd-v10i1.11617. Disponível em: https://rsdjournal.org/index.php/rsd/article/view/11617. Acesso em: 23 jan. 2021.

Issue

Section

Engineerings