Influence of moisture content on bending strength of Sapucaia Wood (Lecythis pisionis cambesse)
DOI:
https://doi.org/10.33448/rsd-v11i11.33158Keywords:
Wood; Moisture content; Flexural strength; MOR; Sapucaia.Abstract
Sapucaia (Lecythis pisionis cambesse) is a species that makes up the botanical family lecythidacea and is commonly found in the Brazilian Amazon, being widely used in heavy internal and heavy external constructions. The objective of this work is to evaluate the influence of the moisture content on the stiffness and flexural strength of sapucaia wood pieces. 18 CPs were used to measure the moisture content using the gravimetric method, with mass measurement at 24-hour intervals and for the bending test, 3 CPs were used per moisture content. With this, it was observed that between 0 and 7 days the measurement of moisture content there was a variation of 13.64% and in the interval between 7 and 14 days there was no significant gain in moisture, with an increase of only 0.61% at the end of the 14 days. In the bending tests, the modulus of rupture (MOR) were obtained, in which the minimum value for 0 days was 94.99 MPa and the maximum value was 118.65 MPa. It was found that the moisture content of the wood, at the time of acquisition, was above the Fiber Saturation Point (29.56%) and its modulus of rupture was 104.36 MPa. In this way, it was possible to verify that the moisture content varied with the submersion time and, as for the average modulus of rupture, it was found that there was no variation.
References
Araújo, H. J. B. (2007). Relações funcionais entre propriedades físicas e mecânicas de madeira tropicais brasileiras. Floresta, Curitiba, PR. set/dez, v. 37, n. 3. doi: 10.5380/rf.v37i3.9937
Associação Brasileira de Normas Técnicas. (2022). NBR 7190 - 1: Projeto de estruturas de madeira. Parte 1: Critérios de dimensionamento. Rio de Janeiro.
Associação Brasileira de Normas Técnicas. (2022). NBR 7190 - 3: Projeto de estruturas de madeira. Parte 3: Métodos de ensaio para corpos de prova isentos de defeitos para madeiras de florestas nativas. Rio de Janeiro.
Almeida, E. & Barbosa, S. E. & Nascimento, F. B. & Santana, F. E. & Sousa, L. F. D. (2020). Estruturas de Madeiras: um novo olhar para a formação acadêmica dos futuros profissionais. Brazilian Journal of Animal and Environmental Research. Curitiba, out/dez, v. 3, n. 4, 3822-3828. doi: 10.34188/bjaerv3n4-082
Anjos, F. P. dos & Sousa, A. M. L. de. (2015). Umidade de Equilíbrio em Madeira Termorretificada de Cupiúba da Região Amazônica. Biota Amazônia Open Journal System, Universidade Federal do Amapá. Macapá – AP, v. 5, n. 1, 99–104. doi: 10.18561/2179-5746/biotaamazonia
Cademartori, G. P. H. & frança, F. R. & Nisgoski, S. & Magalhães, E. L.W. & Muniz, B. I. G. (2013). Característica Anatômica da Madeira de Lecythis pisonis CAMB. I Congresso de Ciência e Tecnologia da madeira (CBCM); III Simpósio de Ciência e Tecnologia do Estado do RJ (SIMADERJ). Rio de Janeiro. Recuperado de https://www.embrapa.br/busca-de-publicacoes/-/publicacao/1004681/caracterizacao-anatomica-da-madeira-de-lecythis-pisonis-camb
Cordeiro, J. et al. (2017). Uso da madeira na construção civil. Projectus, Rio de Janeiro, v. 2, n. 4, 79-93. doi: 10.15202/25254146.2017v2n4p79
Dias, J. M. S. (2018). Estruturas de madeiras. 1. ed. Salvador: 2B Educação.
Dias, J. M. S. et al. (2019). Avaliação comparativa entre métodos de aferição do teor de umidade em peças de madeira de dimensões reduzidas. ResearchGate, Ponta Grossa – PR, v. 3, 171 – 179. doi: 10.22533/at.ed.93019150316
Filho, F. C. L. (2012). Efeito combinado do teor de umidade e da massa específica na resistência e rigidez da madeira de Pinus elliottii. Revista Floresta, v. 42 n. 3, 519–526. doi: 10.5380/rf.v42i3.16973
França, M. C. & Cunha, A. B. da. (2020). Determinação da Relação Resistência / Rigidez e Teor de Umidade da Madeira de Eucalyptus benthamii Maiden et Cambage. Recuperado de https://silo.tips/download/determinaao-da-relaao-resistencia-rigidez-e-teor-de-umidade-da-madeira-de-eucaly#sidebar-close
Gonçalves, F. G. et al. (2009). Estudo de Algumas Propriedades Mecânicas da Madeira de Um Híbrido Clonal de Eucalyptus urophylla X Eucalyptus grandis. R. Árvore, Viçosa-MG, v. 33, n. 3, 501-509. doi: 10.1590/S0100-67622009000300012
Haselein, C. R. et al. (2002). Propriedades de flexão estática da madeira úmida e a 12% de umidade de um clone de Eucalyptus saligna Smith sob o efeito do espaçamento e da adubação. Revista Ciência Florestal, v. 22 n. 2, 147–152. doi: https://doi.org/10.5902/198050981689
INSTITUTO DE PESQUISA TECNOLÓGICA – IPT. (2013). Informações sobre madeiras. Recuperado de https://www.ipt.br/informacoes_madeiras3.php?madeira=73
Lahr, F. A. R. et al. (2015). Avaliação de Propriedades Físicas e Mecânicas de Madeiras de Jatobá (Hymenaea stilbocarpa Hayne) Com Diferentes Teores de Umidade e Extraídas de Regiões Distintas. Revista Árvore, Viçosa-MG, v. 40, n. 1, 147-154. doi: 10.1590/0100-67622016000100016
Melo, R. R. (2013). Estabilidade dimensional de compostos de madeira. Revista Ciência da Madeira (Brazilian Journal of Wood Science), v. 04 n. 02, 152–175. Recuperado de https://periodicos.ufpel.edu.br/ojs2/index.php/cienciadamadeira/article/view/4060
Mendes, L. M. & Arce, J. E. (2003). Análise comparativa das equações utilizadas para estimar a umidade de equilíbrio da madeira. Cerne, Universidade Federal de Lavras. Lavras, Brasil, v. 9, n. 2, jul-dez, 141–152. Recuperado de http://www.bibliotecaflorestal.ufv.br/handle/123456789/18195?show=full
Moreschi, J. C. (2014). Propriedades da madeira. http://www.madeira.ufpr.br/disciplinasmoreschi/PROPRIEDADES%20DA%20MADEIRA.pdf
Moretti, S. D. A. & Santos, C. M. M. dos; Mascarenhas, A. R. P. & Oliveira, J. P. de. & Anjos, S. P. dos. (2020). Avaliação do processo de secagem ao ar livre da madeira de jatobá na Amazônia Evaluation of the outdoor drying process of jatoba wood in the Amazon Evaluación del proceso de secado al aire libre de la madera de jatoba en la Amazonía. Research, Society and Development, [S. l.], 17 ago. v.9, n. n.9, 1-21. doi: 10.33448/rsd-v9i9.7258
Oliveira, J. T. da S. & Silva, J. de C. (2003). Variação radial da retratibilidade e densidade básica da madeira de Eucalyptus saligna Sm. Revista Árvore, v. 27, n. 3, 381 – 385. doi: 10.1590/S0100-67622003000300015
Pelozzi, M. M. A. et al. (2012). Propriedades físicas dos lenhos Juvenil e adulto de Pinus elliottii Engelm var. elliottii E DE Eucalyptus grandis Hill ex Maiden. Revista Ciência Florestal, v. 22 n. 2, 305–313. doi: 10.5902/198050985737
Pereira A. S. et al. (2018). Metodologia da pesquisa científica. [free e-book]. Santa Maria/RS. Ed. UAB/NTE/UFSM. Recuperado de http://repositorio.ufsm.br/handle/1/15824
Ribeiro, R. B. S. & Gama, J. R. V. & Souza, A. L & Andrade, D. F. C. (2019). Análise financeira da extração e beneficiamento de resíduos florestais pós-colheita na floresta nacional do tapajós. Advances in Forestry Science, Cuiabá, v. 6, n. 2, 567-573. doi: 10.34062/afs.v6i2.5621
Santos, L. M. A. (2018). Madeiras. Revista Científica Semana Acadêmica. Fortaleza, ano MMXVIII, Nº. 000131. Recuperado de https://semanaacademica.org.br/artigo/madeiras
Santos, J. O. X. dos. Et al. (2020). Evaluation of physical and mechanical properties of four species of Amazonian wood for use in civil construction. Research, Society and Development, 9(12), e44891211379. doi: 10.33448/rsd-v9i12.11379
Sá, P. A. D & VITO, M. (2014). Estudo da Influência da Umidade nas Propriedades Mecânicas da Madeira. Santa Catarina, SC: UNESC - Universidade do Extremo Sul Catarinense. Recuperado de http://repositorio.unesc.net/handle/1/3020
Silva, V. P. S. & Matos, D. F. & Lima, T. J. & Moreira, W. M. & Dias, J. M. S. (2019). Análise do teor de umidade de madeiras comercializadas na cidade de Açailândia – MA. III Semana de Engenharia Civil – SEC Marabá-PA.
Souza, A. S. de & Margalho, L. & Prance, G. T. & Gurgel, E. S. C. & Gomes, J. I. & Carvalho, L. T. & Martins-da-Silva, R. C. V. (2014). Conhecendo Espécies de Plantas da Amazônia: Sapucaia (Lecythis pisonis Cambess. – Lecythidaceae). Embrapa Amazônia Oriental, Comunicado Técnico, 250. Belém, PA. Recuperado de https://ainfo.cnptia.embrapa.br/digital/bitstream/item/110906/1/COM-250.pdf
Takeshita, S.; Jankowsky, I. P. (2015). Redução na movimentação dimensional da madeira de Jatobá (Hymenaea sp.) e Muiracatiara (Astronium sp.) submetidas a tratamento térmico adicional. Scientia Forestalis, v. 43, n. 106, 345–352. Recuperado de http://www.ipef.br/publicacoes/scientia/nr106/cap10.pdf
Tramontina, J. et al. (2013). PROPRIEDADES DE FLEXÃO ESTÁTICA DA MADEIRA ÚMIDA E A 12% DE UMIDADE DA ESPÉCIE Ateleia glazioviana BAILL. ENCICLOPÉDIA BIOSFERA, 9(16). Recuperado de https://conhecer.org.br/ojs/index.php/biosfera/article/view/3488
Vidal, J. M. el al. (2015). Preservação de madeiras no Brasil: histórico, cenário atual e tendências. Revista Ciência Florestal, v. 25 n.1, 257–271. doi: 10.1590/1980-509820152505257
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2022 Williane Pascoal de Lima Cândido; Ana Paula Gomes Mesquita; Debora Ferreira Matos; Erica dos Santos Lima; Gustavo Santos Ferreira; Paulo Daniel Pimentel Costa; Rafael Moderno Lima; João Miguel Santos Dias
This work is licensed under a Creative Commons Attribution 4.0 International License.
Authors who publish with this journal agree to the following terms:
1) Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
2) Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
3) Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work.